    d.SIGN 59

    Product Number: #B601087
    31g 579910

    d.SIGN 59

    d.SIGN 59 is a palladium-based ceramic alloy. Its low density together with excellent heat resistance enable easy and economical processing and polishing.

    Indications:

  • Onlays, 3/4 crowns, crowns
  • Telescope crowns, conus crowns
  • Bridges
  • Wide-span bridges
  • Cast posts / cores, bars, attachments
  • Implant-supported superstructures
  • Partial dentures
  •  

    Advantages:

  • Excellent heat resistance
  • Economical due to low density
  • Light oxide
  • Excellent processing and polishing properties
  • Compatible with conventional metal-ceramics (eg IPS Style)
  • Certified biocompatibility
  •  

     Composition (%):  Pd 59.2 | Ag 27.9 | Sn 8.2 | In 2.7 | Zn 1.3 | Pt < 1.0 , Re < 1.0, Ru < 1.0, Li < 1.0       
     ISO  22674 : 2016
     ADA Class:  Noble
     Type / Color:  4 / White
     Density (g/cm3)  10.9
     Melting Range (Solidus / Liquidus):     1190 - 1290 C
     Elastic Modulus (GPa):  134
     . Porcelain Fired    Hardened   
     Vickers Hardness:  230 265
     Tensile Strength (Mpa):    740 780
     0.2% Proof Stress (MPa):    490 640
     Elongation (%):  10 5
     Investment Material:  Phosphate - bonded
     Preheating / Burn-out Temperature:     750 - 820 C
     Crucible  Ceramic crucible
     Casting Temperature:  1350 - 1400 C
     Oxidation C / Min / Vacuum:  1010 / 1 / No
     CTE:  (25 - 500 C): 14.5 x 10-6 / K
     Recommended Metal Ceramic:  IPS Style, IPS InLine One, IPS InLine, IPS Classic, IPS d.SIGN   
     Laser Welding Wire:  Laser Ceramic Yellow