    d.SIGN 53

    Product Number: #B601088
    31g 579904

    d.SIGN 53

    d.SIGN 53 is a palladium-based ceramic alloy. Its low density together with excellent flow properties enable easy and economical processing.

    Indications:

  • Onlays, 3/4 crowns, crowns
  • Telescope crowns, conus crowns
  • Bridges
  • Wide-span bridges
  • Cast posts / cores, bars, attachments
  • Implant-supported superstructures
  • Partial dentures
  •  

    Advantages:

  • Good melting and flow properties
  • Economical due to low density
  • Compatible with conventional metal-ceramics (eg IPS Style)
  • Light oxide
  • Certified biocompatibility
  •  

     Composition (%):  Pd 53.8 | Ag 34.9 | Sn 7.7 | In 1.7 | Zn 1.2 | Pt < 1.0 , Re < 1.0, Li < 1.0, Ru < 1.0         
     ISO  22674 : 2016
     ADA Class:  Noble
     Type / Color:  4 / White
     Density (g/cm3)  10.8
     Melting Range (Solidus / Liquidus):     1180 - 1270 C
     Elastic Modulus (GPa):  132
     . Porcelain Fired    Hardened   
     Vickers Hardness:  250 295
     Tensile Strength (Mpa):    730 770
     0.2% Proof Stress (MPa):    545 600
     Elongation (%):  10 10
     Investment Material:  Phosphate - bonded
     Preheating / Burn-out Temperature:     750 - 820 C
     Crucible  Ceramic crucible
     Casting Temperature:  1325 - 1390 C
     Oxidation C / Min / Vacuum:  1010 / 10 / No
     CTE:  (25 - 500 C): 14.8 x 10-6 / K
     Recommended Metal Ceramic:  IPS Style, IPS InLine One, IPS InLine, IPS Classic, IPS d.SIGN   